Q275Enquiry|Print this page
| Category | Type | Steel grade | Country |
|---|---|---|---|
| Grades | Special Alloy | Q275 | China |
Chemical composition%of the ladle analysis of gradeQ275
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) |
|---|---|---|---|---|---|---|---|
| 0.28～0.38 | ≤0.35 | 0.50～0.80 | ≤0.045 | ≤0.050 | ≤0.30 | ≤0.30 | ≤0.30 |
Mechanical properties
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | than 16:275
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:265
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 40 to 60:255
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:245
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:235
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 150:225
Tensile strength σ b/MPa: 490 ~ 630
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | than 16:20
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:19
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 40 to 60:18
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:17
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:16
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 150:15
Impact test (1) | temperature / ℃ :-
Impact test (1) | impact absorption power AKV/J:-
The cold bending property
Sample direction:-
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | than 60: d = 3 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 60 ~ 100: d = 4 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 100 ~ 200: d = 4.5 a
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 171(≥) | 353(≥) | 24 | 23 | 32 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 234 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 766(≥) | 112(≥) | 23 | 14 | 21 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 121 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 468 | 948 | 688 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |