GX120Mn13 Enquiry | Print this page
SEW GX120Mn13 Details
SEW GX120Mn13 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | GX120Mn13 | Germany - SEW , DIN EN 10349 - Steel castings - Austenitic manganese steel castings SEW 395 - Non magnetizable steel casting. Technical delivery conditions |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 1.10 | 1.30 | ||
| Si | - | 0.50 | ||
| Mn | 11.50 | 13.50 | ||
| P | - | 0.060 | ||
| S | - | 0.030 | ||
| Cr | - | 0.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 165 (≥) | 575 (≥) | 32 | 42 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 894 (≥) | 912 (≥) | 13 | 43 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 796 | 688 | 476 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 1.3802 | DIN | Germany | Steel castings - Austenitic manganese steel castings |
| GX120Mn13 | SEW | Germany | Steel castings - Austenitic manganese steel castings |
| X120Mn12, 1.3401, A128, X110Mn14 | EN | European | X120Mn12, 1.3401, A128, X110Mn14 High-manganese steels with austenitic structure, characterized by high carbon content - on average 1.00-1.20%, and high Manganese content - approx. |