Location » Home » Grades > Stainless Steels > ISO H13

ISO ISO H13 Details

Tags

ISO H13 Application:Heat-resistant steels

Category Type Grade Microstructure Designations
Grades Stainless Steels ISO H13 Austenite International - ISO , ISO 15510 (2010) - Stainless steels -- Chemical composition
ISO 4955 (2005) - Heat-resistant steels

Chemical composition(wt.%) of ISO H13 grade: ISO 15510 (2010)

Elements Min.(≥) Max.(≤) Similar Remarks
C - 0.20
Si 1.50 2.50
Mn - 2.00
P - 0.045
S - 0.030
Cr 19.00 21.00
Ni 11.00 13.00
Heat-resistant steels

Mechanical properties of grade ISO H13 ISO 15510 (2010)

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
538 (≥) 555 (≥) 11 42 31 Solution and Aging, Annealing, Ausaging, Q+T,etc 411

Physical properties of grade ISO H13 ISO 15510 (2010)

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
836 (≥) 837 (≥) 34 22 13 Solution and Aging, Annealing, Ausaging, Q+T,etc 234
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
472 951 952

ISO H13 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
ISO H13 ISO International
Heat-resistant steels