10Xl1H20T2P(ЭИ696A) Enquiry | Print this page
GOST 10Xl1H20T2P(ЭИ696A) Details
GOST 10Xl1H20T2P(ЭИ696A) Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | 10Xl1H20T2P(ЭИ696A) | Russia - GOST , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.10 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.020 | ||
| S | - | 0.020 | ||
| Cr | 10.00 | 12.50 | ||
| Ni | 18.00 | 21.00 | ||
| Mo | - | - | ||
| Al | - | 0.50 | ||
| Ti | 2.30 | 2.80 | ||
| Fe | - | remaining | ||
| Cu | - | 0.20 | ||
| B | - | 0.008 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 669 (≥) | 796 (≥) | 23 | 32 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 233 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 871 (≥) | 551 (≥) | 44 | 34 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 672 | 476 | 756 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 10Xl1H20T2P(ЭИ696A) | GOST | Russia | Russia GOCT standard deformation of high temperature alloy grades and chemical composition |