Location » Home » Grades > Stainless Steels > Z12CNDV12-03

AFNOR Z12CNDV12-03 Details

AFNOR Z12CNDV12-03 Standard Download

Z12CNDV12-03 Application:Iron and steel. Stainless steel for high temperature application

Category	Type	Grade	Microstructure	Designations
Grades	Stainless Steels	Z12CNDV12-03	Martensite	France - AFNOR , NF A35-578 - Iron and steel. Stainless steel for high temperature application

Chemical composition(wt.%) of Z12CNDV12-03 grade: NF A35-578

Elements	Min.（≥）	Max.（≤）
C	0.08	0.13
Si	-	0.40
Mn	0.50	0.90
P	-	0.030
S	-	0.025
Cr	11.00	12.50
Ni	2.00	4.00
N	0.020	0.040
V	0.25	0.40

Z 12 CNDV 12-03 is a new type of martensitic stainless steel for the last-stage blades of large-capacity nuclear and thermal power turbines. The deformation behavior of this steel was studied by thermal compression experiments that performed on a Gleeble-3500 thermal simulator at a temperature range of 850°C to 1200°C and a strain rate of 0.01s-1 to 20s-1. When the deformation was performed at high temperature and low strain rate, a necklace type of microstructures was observed, the plastic deformation mechanism is grain boundary slip and migration, when at low temperature and lower strain rate, the slip bands were observed, the mechanism is intracrystalline slips, and when at strain rate of 20s-1, twins were observed, the mechanism are slips and twins. The Arrhenius equation was applied to describe the constitutive equation of the flow stress. The accuracy of the equation was verified by using the experimental data and the correlation coefficient R2 = 0.9786, and the equation can provide reasonable data for the design and numerical simulation of the Z12CNDV12-03 forging process.

Mechanical properties of grade Z12CNDV12-03 NF A35-578

Proof strength R_p0.2 (MPa)	Tensile strength R_m (MPa)	Impact energy KV (J)	Elongation at fracture A (%)	Reduction in cross section on fracture Z (%)	As-Heat-Treated Condition	Brinell hardness (HBW)
545 (≥)	745 (≥)	33	34	31	Solution and Aging, Annealing, Ausaging, Q+T,etc	412

Physical properties of grade Z12CNDV12-03 NF A35-578

Property	Density kg/dm3	Temperature T °C/F	Specific heat J / kgK	Thermal conductivity W/mK	Electric resistance µΩ·cm	Modulus of elasticity kN/mm2
962 (≥)	316 (≥)	42	32	13	Solution and Aging, Annealing, Ausaging, Q+T,etc	234
Temp. °C/°F	Creep strain limit (10000h) (Rp1,0) N/mm2	Creep rupture strength (10000h) (Rp1,0) N/mm2
676	811	335

Z12CNDV12-03 - Form of Supply

Product type	Products	Dimension	Processes	Deliver Status
Plates / Sheets	Plates / Sheets	0.08-200mm(T)WL	Forging, hot rolling and cold rolling	Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar	Round Bar, Flat Bar, Square Bar	Φ8-1200mm*L	Forging, hot rolling and cold rolling, Cast	Black, Rough Turning, Shot Blasting,
Coil / Strip	Steel Coil /Steel Strip	0.03-16.0x1200mm	Cold-Rolled & Hot-Rolled	Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes	Seamless Pipes/Tubes, Welded Pipes/Tubes	OD:6-219mm x WT:0.5-20.0mm	Hot extrusion, Cold Drawn, Welded	Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade	Standard	Country	Application
Z12CNDV12-03	AFNOR	France	Iron and steel. Stainless steel for high temperature application
Z12CNDV12-03	AFNOR	France	Iron and steel. Stainless steel for high temperature application
Z12CNDV12-03	AFNOR	France	Iron and steel. Stainless steel for high temperature application
Z12CNDV12 Air 9160/C	AFNOR	France	wrought steels used in aeronautical constructions