SAE T7 Details
SAE T7 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Tool Die Steels | T7 | USA - SAE , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.70 | 0.75 | ||
| Si | 0.20 | 0.40 | ||
| Mn | 0.20 | 0.40 | ||
| Cr | 4.50 | 5.00 | ||
| Mo | - | - | ||
| V | 1.50 | 1.80 | ||
| W | 13.50 | 14.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 726 (≥) | 843 (≥) | 24 | 32 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 244 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 542 (≥) | 711 (≥) | 11 | 12 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 676 | 711 | 996 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| T72301 | AISI | USA | Carbon tool steel products which include hot or cold finished bar, plate, sheet, rod, wire, or forgings, which are normally fabricated into tools, dies, or fixtures. |
| W2-A | SAE | USA | Carbon tool steel products which include hot or cold finished bar, plate, sheet, rod, wire, or forgings, which are normally fabricated into tools, dies, or fixtures. |
| T72302 | AISI | USA | Carbon tool steel products which include hot or cold finished bar, plate, sheet, rod, wire, or forgings, which are normally fabricated into tools, dies, or fixtures. |
| T72305 | AISI | USA | Carbon tool steel |
| Udimet 700 | SAE | USA | Special Purpose Alloys ("Superalloys") |
| T7 | SAE | USA | High-Speed Tool Steel |