1.2080 Enquiry | Print this page
EN 1.2080 Details
EN 1.2080 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Tool Die Steels | 1.2080 | Germany - EN , DIN 17350 (1980) - Tool Steels; Technical Conditions of Delivery DIN EN ISO 4957 (1999) - Tool steels (ISO 4957:1999) |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 1.90 | 2.20 | ||
| Si | 0.10 | 0.40 | ||
| Mn | 0.15 | 0.45 | ||
| P | - | 0.030 | ||
| S | - | 0.030 | ||
| Cr | 11.00 | 12.00 | ||
| Mo | - | - | ||
| V | - | - |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 266 (≥) | 641 (≥) | 11 | 14 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 314 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 125 (≥) | 827 (≥) | 11 | 41 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 112 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 995 | 198 | 176 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 1.2080 | EN | Germany | Tool steels (ISO 4957:1999) |
| Cr12 | GB | China | Often used in the manufacture of small bear impact load and wear resistance of high cold cold punching die, punch, shear knife, cold roll, drill sets and wire drawing die, as well as the gauge, model, the CAM pin, eccentric wheel, etc |