F10004 Enquiry | Print this page
AISI F10004 Details
AISI F10004 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Cast Iron and Cast Steel | F10004 | Ferrite-Pearlitic | USA - AISI , A 159 (2011) - Automotive Gray Iron Castings |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 3.40 | 3.70 | ||
| Si | 2.30 | 2.80 | ||
| Mn | 0.50 | 0.80 | ||
| P | - | 0.25 | ||
| S | - | 0.15 | ||
| CEV | 4.25 | 4.5 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 434 (≥) | 281 (≥) | 21 | 34 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 413 (≥) | 721 (≥) | 23 | 12 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 327 | 213 | 172 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| F10004 | AISI | USA | Used in the products of the automobile, truck, tractor, and allied industries. Miscellaneous soft iron castings (as cast or annealed) in which strength is not of primary consideration. Exhaust manifolds may be made of this grade of iron, alloyed or unallo |