ГОСТ у9-3Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | у9-3 | ГОСТ | Russia |
Chemical composition%of the ladle analysis of gradeу9-3
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) |
|---|---|---|---|---|---|---|---|
| 0.85-0.94 | 0.17-0.33 | 0.17-0.33 | ≤0.030 | ≤0.028 | 0.20-0.40 | ≤0.25 | 0.20 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 779(≥) | 666(≥) | 23 | 23 | 44 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 212 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 443(≥) | 693(≥) | 21 | 22 | 42 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 314 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 766 | 317 | 187 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X45CrSi9-3 | ГОСТ | Russia | Valve steels and alloys for internal combustion engines |
| 1.4718 | ГОСТ | Russia | Valve steels and alloys for internal combustion engines |
| X45CrSi9-3 | ГОСТ | Russia | Heat-treatable steels, alloy steels and free-cutting steels -- Part 15: Valve steels for internal combustion engines |
| X30WCrV9-3, 1.2581, Z30WCV9, H21 | ГОСТ | Russia | Tool steel for hot work with high content of tungsten according |