AFNOR Z4CNDAT13-09Enquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | Z4CNDAT13-09 | AFNOR | France |
Chemical composition%of the ladle analysis of gradeZ4CNDAT13-09
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | Al(%) | Ti(%) |
|---|---|---|---|---|---|---|---|---|---|
| Max 0.04 | Max 0.10 | Max 0.20 | Max 0.015 | Max 0.008 | 11.5-13.5 | 7.50-9.50 | 1.80-2.50 | 0.60-1.40 | Max 0.40 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 273(≥) | 612(≥) | 21 | 44 | 12 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 412 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 396(≥) | 896(≥) | 12 | 44 | 33 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 342 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 926 | 642 | 678 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| Z4CNDAT13-09 | AFNOR | France | Medico-surgical equipment - Materials for ancillary positioning instruments for surgical instrument - Martensitic, precipitation hardening, austenitic and austeno-ferritic stainless steels |