Grades | Special Alloy | Z6CNDT17-13B | AFNOR | France |
Chemical composition%of the ladle analysis of gradeZ6CNDT17-13B
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Mo(%) | B(%) | Ti(%) |
---|---|---|---|---|---|---|---|---|
0.04-0.08 | Max 0.75 | Max 2.00 | Max 0.040 | Max 0.015 | 16.0-18.0 | 12.0-14.0 | 0.0015-0.0060 | 4(C+N) Max 0.70 |
Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
---|---|---|---|---|---|---|
446(≥) | 459(≥) | 41 | 23 | 21 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 123 |
Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
---|---|---|---|---|---|---|---|
673(≥) | 519(≥) | 22 | 14 | 14 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 123 | |
Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
621 | 141 | 578 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
Z6CNDT17-13B | AFNOR | France | Iron and steel. Stainless steel for high temperature application |