T9Enquiry|Print this page
| Category | Type | Steel grade | Country |
|---|---|---|---|
| Grades | Special Alloy | T9 | China |
Chemical composition%of the ladle analysis of gradeT9
| C(％) | Si(％) | Mn(％) | P(％) | S(％) |
|---|---|---|---|---|
| 0.85～0.94 | ≤0.35 | ≤0.40 | ≤0.035 | ≤0.030 |
The performance characteristics of carbon steel and use
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 488(≥) | 956(≥) | 23 | 21 | 13 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 111 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 799(≥) | 595(≥) | 12 | 42 | 13 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 221 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 956 | 572 | 996 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| T9 | China | High-Speed Tool Steel | |
| X10CrWMoVNb9 | China | Boiler tubes are used in heat exchange appliances in which the energy is transferred from one medium to the other. The pipes are manufactured from carbon and low-alloy steel grades which are resistant to loads under high pressure and temperatures. They ar |