Q235 DEnquiry|Print this page
| Category | Type | Steel grade | Country |
|---|---|---|---|
| Grades | Special Alloy | Q235 D | China |
Chemical composition%of the ladle analysis of gradeQ235 D
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Cu(%) |
|---|---|---|---|---|---|---|---|
| ≤0.17 | ≤0.30 | 0.35～0.80 | 0.035 | 0.030 | ≤0.30 | ≤0.30 | ≤0.30 |
Mechanical properties
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | ≤ 16:235
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:225
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 40 to 60:215
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:205
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:195
The yield point σ s/MPa (no less) than in steel different thickness or diameter/mm | > 150:185
Tensile strength σ b/MPa: 375 ~ 450
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | than 16:26
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 16 ~ 40:25
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 40 to 60:24
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 60 ~ 100:23
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 100 ~ 150:22
Elongation δ 5 / (%) (no less) than in steel different thickness or diameter/mm | > 150:21
Impact test (1) | temperature / ℃ :-20
Impact test (1) | impact absorption power AKV/J: 27 frequency
The cold bending property
Sample direction: horizontal180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | than 60: d = 1.5 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 60 ~ 100: d = 2.5 a
180 ° of cold bending test b = 2 a different thickness or in steel diameter/mm | > 100 ~ 200: d = 3 a
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 594(≥) | 521(≥) | 23 | 13 | 44 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 432 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 123(≥) | 341(≥) | 24 | 44 | 22 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 132 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 297 | 759 | 412 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |