7Mn15Cr2A13V2WMoEnquiry|Print this page
| Category | Type | Steel grade | Country |
|---|---|---|---|
| Grades | Special Alloy | 7Mn15Cr2A13V2WMo | China |
Chemical composition%of the ladle analysis of grade7Mn15Cr2A13V2WMo
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) | W(%) | Al(%) |
|---|---|---|---|---|---|---|---|---|---|
| 0.65～0.75 | ≤0.80 | 14.50～16.50 | ≤0.030 | ≤0.030 | 2.00～2.50 | 0.50～0.80 | 1.50～2.00 | 0.50～0.80 | 2.30～3.30 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 914(≥) | 163(≥) | 21 | 11 | 22 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 132 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 516(≥) | 876(≥) | 41 | 14 | 43 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 432 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 932 | 198 | 396 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |