EN EN X6CrNiTiB18-10Enquiry|Print this page
Category | Type | Steel grade | Standard | Country |
---|---|---|---|---|
Grades | Special Alloy | EN X6CrNiTiB18-10 | EN | Euronorm |
Chemical composition%of the ladle analysis of gradeEN X6CrNiTiB18-10
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Ti(%) |
---|---|---|---|---|---|---|---|
0.04-0.08 | 1.00 | 2.00 | 0.035 | 0.015 | 17.0-19.0 | 9.00-12.0 | 5xC-0.80 |
Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
---|---|---|---|---|---|---|
341(≥) | 973(≥) | 21 | 11 | 11 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 442 |
Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
---|---|---|---|---|---|---|---|
236(≥) | 864(≥) | 23 | 12 | 13 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 432 | |
Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
188 | 133 | 944 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
X6CrNiTiB18-10 | EN | Euronorm | Creep resisting steels, nickel and cobalt alloys |
1.4941 | EN | Euronorm | Creep resisting steels, nickel and cobalt alloys |