GBT GH1016Enquiry|Print this page
Category | Type | Steel grade | Standard | Country |
---|---|---|---|---|
Grades | Special Alloy | GH1016 | GBT | China |
Chemical composition%of the ladle analysis of gradeGH1016
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | V(%) | W(%) | N(%) | B(%) | Nb(%) | Other(%) |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
0.08 | 0.60 | 1.80 | 0.020 | 0.015 | 19.0-22.0 | 32.0-36.0 | 2.60-3.30 | 0.10-0.30 | 5.00-6.00 | 0.13-0.25 | 0.01 Max | 0.90-1.40 | Fe:Balance; Ce≤0.05 |
Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
---|---|---|---|---|---|---|
623(≥) | 395(≥) | 13 | 22 | 12 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 111 |
Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
---|---|---|---|---|---|---|---|
949(≥) | 483(≥) | 11 | 31 | 41 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 113 | |
Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
161 | 767 | 834 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
GH1016 | GBT | China | Classification and designation for superalloys and high temperature intermetallic materials |