B.S. 442S19Enquiry|Print this page
Category | Type | Steel grade | Standard | Country |
---|---|---|---|---|
Grades | Special Alloy | 442S19 | B.S. | UK |
Chemical composition%of the ladle analysis of grade442S19
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | Ni(%) | Mo(%) | V(%) | W(%) | Cu(%) | Other(%) |
---|---|---|---|---|---|---|---|---|---|---|---|
0.20-0.25 | 0.20-0.60 | 1.0 | 0.040 | 0.030 | 11.0-13.5 | 0.50-1.0 | 0.75-1.25 | 0.17-0.30 | 0.75-1.25 | 0.50 | Fe:Balance; |
UNS S42200
AISI 616
AMS 5655 Bars / wire/ forging H&T
ASTM A 565 GRD 616
DOD F 24669/7
MIL S 861
B50A125 (Cap of)
B50A951A1 (Cap of)
BS 970; 442S19
EN61
Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
---|---|---|---|---|---|---|
468(≥) | 977(≥) | 24 | 44 | 34 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 442 |
Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
---|---|---|---|---|---|---|---|
758(≥) | 962(≥) | 24 | 44 | 14 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 143 | |
Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
385 | 875 | 477 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |