GBT 0Cr17Ni7AlEnquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | 0Cr17Ni7Al | GBT | China |
Chemical composition%of the ladle analysis of grade0Cr17Ni7Al
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Other(%) |
|---|---|---|---|---|---|---|---|
| Max 0.09 | Max 1.00 | Max 1.00 | 0.035 | Max 0.03 | 16.00-18.00 | 6.50-7.75 | Al 0.75-1.50 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 747(≥) | 774(≥) | 31 | 34 | 32 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 143 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 655(≥) | 335(≥) | 14 | 33 | 43 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 432 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 235 | 648 | 132 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 0Cr17Ni7Al | GBT | China | Heat-resisting steel sheets and plates |
| 0Cr17Ni7Al | GBT | China | Heat-resisting steel sheets and plates |
| S63198 | GBT | China | Iron Base Superalloy |
| A 313 S17700 | GBT | China | Stainless Steel Spring Wire |
| A 564 S17700 | GBT | China | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| A 693 S17700 | GBT | China | Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| A 705 S17700 | GBT | China | Age-Hardening Stainless Steel Forgings |
| S17700 | GBT | China | Precipitation Hardenable Chromium Nickel Aluminum Stainless Steel |
| SA-564 S17700 | GBT | China | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| SA-693 S17700 | GBT | China | Specification for Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| SA-705 S17700 | GBT | China | Specification for Age-Hardening Stainless Steel Forgings |
| S63198 | GBT | China | Iron Base Superalloy |
| A 313 S17700 | GBT | China | Stainless Steel Spring Wire |
| A 564 S17700 | GBT | China | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
| A 693 S17700 | GBT | China | Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip |
| A 705 S17700 | GBT | China | Age-Hardening Stainless Steel Forgings |
| S17700 | GBT | China | Precipitation Hardenable Chromium Nickel Aluminum Stainless Steel |
| SA-564 S17700 | GBT | China | Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes |
Relevant products
0Cr17Ni7Al Steel Stock
| Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
|---|---|---|---|---|---|---|
| 17-7PH / 631 Coil & Strip, Sheet Stock | 0.3-3.0*10-180mm | Coil or Strip | Kgs | 1236.22 | Cold-Rolled+Annealed | Enquiry |