ГОСТ XH55BMTKЮEnquiry|Print this page
Category | Type | Steel grade | Standard | Country |
---|---|---|---|---|
Grades | Special Alloy | XH55BMTKЮ | ГОСТ | Russia |
Chemical composition%of the ladle analysis of gradeXH55BMTKЮ
C(%) | Si(%) | Mn(%) | Cr(%) | Ni(%) | Mo(%) | V(%) | W(%) | Co(%) | B(%) | Al(%) | Ti(%) |
---|---|---|---|---|---|---|---|---|---|---|---|
0.04-0.10 | Max 0.50 | Max 0.50 | 9.0-12.0 | Balance | 4.00-6.00 | 0.20-0.80 | 4.50-6.50 | 12.0-16.0 | Max 0.02 | 3.60-4.50 | 1.40-2.00 |
Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
---|---|---|---|---|---|---|
475(≥) | 622(≥) | 42 | 11 | 11 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 124 |
Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
---|---|---|---|---|---|---|---|
369(≥) | 861(≥) | 32 | 11 | 31 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 344 | |
Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
641 | 733 | 328 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
XH55BMTKЮ | ГОСТ | Russia | Russia GOCT standard deformation of high temperature alloy grades and chemical composition |