ГОСТ XH62MBKЮ-BДEnquiry|Print this page
| Category | Type | Steel grade | Standard | Country |
|---|---|---|---|---|
| Grades | Special Alloy | XH62MBKЮ-BД | ГОСТ | Russia |
Chemical composition%of the ladle analysis of gradeXH62MBKЮ-BД
| C(％) | Si(％) | Mn(％) | Cr(％) | Ni(％) | Mo(％) | W(%) | Co(%) | B(%) | Al(%) | Other(%) |
|---|---|---|---|---|---|---|---|---|---|---|
| Max 0.10 | Max 0.25 | Max 0.30 | 8.5-10.5 | Balance | 9.00-11.5 | 4.30-5.50 | 4.00-5.50 | Max 0.02 | 4.20-4.90 | Ce: Max 0.02 |
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 137(≥) | 851(≥) | 42 | 11 | 42 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 312 |
| Property | Density kg/dm3 | Temperature T °C/F | Specific heat J/kgK | Thermal conductivity W/mK | Electric resistance µΩ·cm | Modulus of elasticity kN/mm2 | Expansion rate |
|---|---|---|---|---|---|---|---|
| 311(≥) | 676(≥) | 42 | 23 | 34 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 211 | |
| Temp. °C/°F | Creep strain limit (10000h) (Rp1,0)N/mm2 | Creep rupture strength (10000h) (Rp1,0)N/mm2 | |||||
| 638 | 871 | 131 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| XH62MBKЮ-BД | ГОСТ | Russia | Russia GOCT standard deformation of high temperature alloy grades and chemical composition |