Home»Grades > Special Alloy > ЖC3-BИ
ЖC3-BИApplication:Vacuum melting of casting high temperature alloy rod
CategoryTypeSteel gradeStandardCountry
Grades Special Alloy ЖC3-BИГОСТRussia

Chemical composition%of the ladle analysis of gradeЖC3-BИ

C(%)Cr(%)Ni(%)Mo(%)W(%)Al(%)Ti(%)
0.11-0.1614.0-18.0Balance3.0-4.54.5-6.51.6-2.21.6-2.3
ЖC3-BИ
Mechanical properties of gradeЖC3-BИ
Proof strength
Rp0.2(MPa)
Tensile strength
Rm(MPa)
Impact energy
KV(J)
Elongation at fracture
A(%)
Reduction in cross section on fracture
Z(%)
As-Heat-Treated ConditionBrinell hardness(HBW)
712(≥)816(≥)243423Solution and Aging,Annealing,Ausaging,Q+T,etc422
Physical properties of gradeЖC3-BИ
PropertyDensity
kg/dm3
Temperature T
°C/F
Specific heat
J/kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
286(≥)999(≥)243212Solution and Aging,Annealing,Ausaging,Q+T,etc121
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0)N/mm2
Creep rupture strength
(10000h)
(Rp1,0)N/mm2
168213254
ЖC3-BИRange of products
Product typeProductsDimensionProcessesDeliver Status
Plates/SheetsPlates/Sheets0.08-200mm(T)*W*LForging,hot rolling and cold rollingAnnealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Steel BarRound Bar,Flat Bar,Square BarΦ8-1200mm*LForging,hot rolling and cold rolling,CastBlack,Rough Turning,Shot Blasting,
Coil/StripSteel Coil/Steel Strip0.03-16.0x1200mmCold-Rolled&Hot-RolledAnnealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting
Pipes/TubesSeamless Pipes/Tubes,Welded Pipes/TubesOD:6-219mm x WT:0.5-20.0mmHot extrusion,Cold Drawn,WeldedAnnealed,Solution and Aging,Q+T,ACID-WASHED
Cross Reference Table(Equivalent Grade)
GradeStandardCountryApplication
ЖC3-BИГОСТRussia
Russia GOCT Standard vacuum smelting casting high temperature alloy bar
ЖC3-BИГОСТRussia
Russia GOCT Standard vacuum smelting casting high temperature alloy bar

Enquiry

Please enter the kg or metric tons.
Please be sure to fill in, in order to contact!
Please be sure to fill in, in order to contact!
Please fill in the Size, Quantity, Weight,, etc...

* Required fields