GH1013 Enquiry | Print this page
GB GH1013 Details
GB GH1013 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Superalloys | GH1013 | China - GB , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.06 | ||
| Cr | - | 20.0 | ||
| Mo | - | 1.5 | ||
| Ni | - | 25.0 | ||
| Nb | - | 0.8 | ||
| Ti | - | 0.8 | ||
| B | - | 0.01 | ||
| Fe | - | Remainder | ||
| Mn | - | 1.9 | ||
| Ce | - | 0.05 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 744 (≥) | 532 (≥) | 13 | 32 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 323 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 115 (≥) | 324 (≥) | 32 | 32 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 414 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 739 | 143 | 232 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH1013 | GB | China | Iron-based Superalloy |