Location » Home » Grades > Superalloys > GH 3536

JB GH 3536 Details

GH 3536 Application:Superalloy GH536 is a kind of added tungsten cobalt and nickel - chromium - molybdenum alloy.GH536 alloy at 1200 ℃ with excellent oxidation resistance at high temperature, also can be applied to the neutral and reducing atmosphere.At the same time GH536 a

Category Type Grade Designations
Grades Superalloys GH 3536 China - JB ,

Chemical composition(wt.%) of GH 3536 grade:

Elements Min.(≥) Max.(≤) Similar Remarks
Ni - Bal
Cr 20.50 23.50
Fe 17.00 20.00
C 0.05 0.15
Mn - 1.00
Si - 1.00
Mo 8.00 10.00
Co 0.50 2.50
Al - 0.10
W 0.20 1.00
B - 0.005
P - 0.015
S - 0.01
When up to 1200 ℃ with excellent oxidation resistance
Low good high temperature strength
"Very good formability and weldability
"Very good resistance to stress corrosion cracking
Due to high temperatures in all kinds of atmosphere corrosion resistance, and has excellent high temperature strength, GH536 has been widely used in various high temperature environment.
Typical applications:
Low industrial and aviation turbine (combustion chamber, the structure of the rectifier, cover)
Low industrial furnace parts, supporting roller, grating, ribbons and radiant tube
Low oil chemical spiral tube in the furnace
Low high temperature gas cooled reactor

Mechanical properties of grade GH 3536

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
726 (≥) 797 (≥) 24 44 33 Solution and Aging, Annealing, Ausaging, Q+T,etc 412

Physical properties of grade GH 3536

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
813 (≥) 488 (≥) 11 31 44 Solution and Aging, Annealing, Ausaging, Q+T,etc 442
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
578 298 441

GH 3536 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
GH 3536 JB China
Superalloy GH536 is a kind of added tungsten cobalt and nickel - chromium - molybdenum alloy.GH536 alloy at 1200 ℃ with excellent oxidation resistance at high temperature, also can be applied to the neutral and reducing atmosphere.At the same time GH536 a