Location » Home » Grades > Superalloys > MONEL K-500

MONEL K-500 Enquiry | Print this page

Whole MONEL K-500 Details

Whole MONEL K-500 Standard Download

Tags

MONEL K-500 Application:Mainly used in the manufacture of aircraft engine working temperature in turbine blade and gas turbine blade below 750 DEG C; for fasteners

Category Type Grade Designations
Grades Superalloys MONEL K-500 - ,

Chemical composition(wt.%) of MONEL K-500 grade:

Elements Min.（≥） Max.（≤） Similar Remarks
Ni 63.00 -
C - 0.25
Mn - 1.50
Fe - 2.00
S - 0.01
Si - 0.50
Cu 27.00 33.00
Al 2.30 3.15
Ti 0.35 0.85
Mainly used in the manufacture of aircraft engine working temperature in turbine blade and gas turbine blade below 750 DEG C; for fasteners, manufacturing ship spring; chemical equipment of the pump, valve parts; papermaking equipment on the scraping blade.

Mechanical properties of grade MONEL K-500

Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
926 (≥) 892 (≥) 42 31 41 Solution and Aging, Annealing, Ausaging, Q+T,etc 411

Physical properties of grade MONEL K-500

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
854 (≥) 798 (≥) 23 33 41 Solution and Aging, Annealing, Ausaging, Q+T,etc 322
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
664 128 778

MONEL K-500 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
MONEL K-500 Whole Whole
Mainly used in the manufacture of aircraft engine working temperature in turbine blade and gas turbine blade below 750 DEG C; for fasteners

Enquiry