T41904 Enquiry | Print this page
UNS T41904 Details
UNS T41904 Standard Download
Category | Type | Grade | Designations |
---|---|---|---|
Grades | Tool Die Steels | T41904 | USA - UNS , |
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | 0.50 | 0.65 | ||
Si | 1.75 | 2.25 | ||
Mn | 0.60 | 0.95 | ||
P | - | 0.030 | ||
S | - | 0.030 | ||
Cr | 0.10 | 0.50 | ||
Mo | - | - | ||
V | 0.15 | 0.35 | ||
W | - | - | ||
Ni+Cu | - | 0.75 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
782 (≥) | 523 (≥) | 41 | 42 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
776 (≥) | 232 (≥) | 42 | 21 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 444 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
594 | 411 | 262 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
T41904 | UNS | USA | Shock-Resisting Tool Steel |