Location » Home » Grades > Tool Die Steels > L7

SAE L7 Details

Tags

L7 Application:Low Alloy Tool Steel

Category Type Grade Designations
Grades Tool Die Steels L7 USA - SAE ,

Chemical composition(wt.%) of L7 grade:

Elements Min.(≥) Max.(≤) Similar Remarks
C 0.95 1.05
Si 0.20 0.40
Mn 0.25 0.45
Cr 1.25 1.75
Mo 0.30 0.50
V - -
W - -
Low Alloy Tool Steel

Mechanical properties of grade L7

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
835 (≥) 977 (≥) 43 11 33 Solution and Aging, Annealing, Ausaging, Q+T,etc 231

Physical properties of grade L7

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
482 (≥) 581 (≥) 32 21 24 Solution and Aging, Annealing, Ausaging, Q+T,etc 113
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
568 829 561

L7 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
EVll UNS USA
Steel for exhaust valves
S63011 AISI USA
Steel for exhaust valves
EVl7 UNS USA
Steel for exhaust valves
HEV2 UNS USA
Steel for exhaust valves
N07002 AISI USA
Steel for exhaust valves
L7 SAE USA
Low Alloy Tool Steel

Enquiry