DIN 1.2004 Details

DIN 1.2004 Standard Download

Tags

1.2004 Application:Low alloyed Cr steel

Category Type Grade Designations
Grades Tool Die Steels 1.2004 Germany - DIN ,

Chemical composition(wt.%) of 1.2004 grade:

Elements Min.（≥） Max.（≤） Similar Remarks
C 0.80 0.90
Si 0.30 0.50
Mn 0.50 0.70
P - 0.035
S - 0.035
Cr 0.30 0.45
Mo - -
V - -
Low alloyed Cr steel

Mechanical properties of grade 1.2004

Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
584 (≥) 519 (≥) 21 14 34 Solution and Aging, Annealing, Ausaging, Q+T,etc 214

Physical properties of grade 1.2004

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
449 (≥) 769 (≥) 13 13 13 Solution and Aging, Annealing, Ausaging, Q+T,etc 343
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
825 381 773

1.2004 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
1.2004 DIN Germany
Low alloyed Cr steel

Enquiry