Location » Home » Grades > Tool Die Steels > 105WCr6

DIN 105WCr6 Details

Tags

105WCr6 Application:Tool Steels; Technical Conditions of Delivery

Category Type Grade Designations
Grades Tool Die Steels 105WCr6 Germany - DIN , DIN 17350 (1980) - Tool Steels; Technical Conditions of Delivery

Chemical composition(wt.%) of 105WCr6 grade: DIN 17350 (1980)

Elements Min.(≥) Max.(≤) Similar Remarks
C 1.00 1.10
Si 0.10 0.40
Mn 0.80 1.10
P - 0.030
S - 0.030
Cr 0.90 1.10
Mo - -
V - -
W 1.00 1.30
Tool Steels; Technical Conditions of Delivery

Mechanical properties of grade 105WCr6 DIN 17350 (1980)

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
928 (≥) 988 (≥) 43 14 14 Solution and Aging, Annealing, Ausaging, Q+T,etc 223

Physical properties of grade 105WCr6 DIN 17350 (1980)

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
522 (≥) 255 (≥) 33 42 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 244
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
366 465 348

105WCr6 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
105WCr6 DIN Germany
Tool Steels; Technical Conditions of Delivery