142WV13 Enquiry | Print this page
DIN 142WV13 Details
DIN 142WV13 Standard Download
Category | Type | Grade | Designations |
---|---|---|---|
Grades | Tool Die Steels | 142WV13 | Germany - DIN , |
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | 1.35 | 1.50 | ||
Si | 0.15 | 0.30 | ||
Mn | 0.20 | 0.40 | ||
P | - | 0.035 | ||
S | - | 0.035 | ||
Cr | 0.20 | 0.50 | ||
Mo | - | - | ||
V | 0.20 | 0.30 | ||
W | 2.80 | 3.30 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
392 (≥) | 658 (≥) | 11 | 13 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 132 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
769 (≥) | 778 (≥) | 34 | 41 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
317 | 523 | 716 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
142WV13 | DIN | Germany | Alloyed WV steel |