AISI A-2 Details
AISI A-2 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Tool Die Steels | A-2 | USA - AISI , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.95 | 1.05 | ||
| Si | - | 1.00 | ||
| Mn | - | 0.50 | ||
| Cr | 4.75 | 5.50 | ||
| Mo | 0.90 | 1.40 | ||
| V | 0.15 | 0.50 | ||
| Ni | - | 0.30 |
Good combination of wear resistance and toughness. Very stable in heat treatment.
Not difficult to machine or grind.
Good Hardenability.
AVAILABILITY
Readily available
MACHINABILITY
A-2 can be machined readily in the fully annealed condition. Its machinability rating is about 65% of a 1% carbon tool steel. It also has a high grindability rating.
ANNEALING
Heat slowly to 1500 to 1600°F and furnace cool, allowing the temperature to drop about 75°Fper hour to 1000°F. Then air cool. The annealed hardness is 202 to 248 Brinell.
HARDENING
A-2 should be preheated at 1200° to 1300°F then taken up to 1725° to 1750°F. When part is at temperature it should be soaked 30 minutes for the first inch of thickness and 15 minutes for each inch of thickness over one inch. If a controlled atmosphere or vacuum furnace is not available then part should be wrapped in stainless foil to prevent decarburization. When the piece is taken from the furnace the stainless foil must be removed (if applicable) and then cooled in still air. Large pieces may require forced air.
TEMPERING
As soon as pieces have been cooled to room temperature (100° to 125°F) tempering must begin. Heat slowly to the tempering temperature selected to obtain the hardness desired. Double tempering is recommended.
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 678 (≥) | 321 (≥) | 31 | 12 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 736 (≥) | 925 (≥) | 12 | 14 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 737 | 375 | 995 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A-2 | AISI | USA | Applied to the thermosetting plastic mold, the hardened mould as a whole |
| HEV7 | UNS | USA | Steel for exhaust valves |
Relevant products
A-2 Steel Stock
| Steel grade | Dimension | Shape | Unit | Quantity | Delivery state | Query |
|---|---|---|---|---|---|---|
| IncoloyA-286 / GH 2132 Stock | Φ8-65mm*L | Round Bar | Kgs | 489 | Hot-Rolled+Annealed+black | Enquiry |