26NiCrMoV14-5 Enquiry | Print this page
SEW 26NiCrMoV14-5 Details
SEW 26NiCrMoV14-5 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Tool Die Steels | 26NiCrMoV14-5 | Austenite | Germany - SEW , SEW 555 - Steels for larger forgings for components in turbine and generator installations |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.28 | ||
| Si | - | 0.25 | ||
| Mn | - | 0.40 | ||
| P | - | 0.010 | ||
| S | - | 0.010 | ||
| Cr | 1.40 | 1.80 | ||
| Ni | 3.40 | 3.80 | ||
| Mo | 0.30 | 0.45 | ||
| V | - | 0.15 | ||
| Al | - | 0.025 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 449 (≥) | 412 (≥) | 42 | 11 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 883 (≥) | 682 (≥) | 21 | 44 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 341 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 267 | 898 | 651 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 26NiCrMoV14-5 | SEW | Germany | Steels for larger forgings for components in turbine and generator installations |
| 1.6957 | DIN | Germany | Steels for larger forgings for components in turbine and generator installations |