Location » Home » Grades > Aviation and Aero Steel > AMS 6305F 17-22A
AMS AMS 6305F 17-22A Details
AMS AMS 6305F 17-22A Standard Download
AMS 6305F 17-22A Application:Steel, Heat-Resistant, Bars, Forgings, and Tubing 0.95Cr - 0.55Mo - 0.30V (0.40 - 0.50C) Vacuum Arc Remelted
| Category |
Type |
Grade |
Designations |
| Grades | Aviation and Aero Steel | AMS 6305F 17-22A |
USA - AMS , AM S6305-2012 - Steel, Heat-Resistant, Bars, Forgings, and Tubing 0.95Cr - 0.55Mo - 0.30V (0.40 - 0.50C) Vacuum Arc Remelted
|
Chemical composition(wt.%) of AMS 6305F 17-22A grade: AM S6305-2012
| Elements |
Min.（≥） |
Max.（≤） |
Similar |
Remarks |
| C |
0.40 |
0.50 |
|
|
| Si |
0.15 |
0.35 |
|
|
| Mn |
0.40 |
0.70 |
|
|
| P |
- |
0.015 |
|
|
| S |
- |
0.015 |
|
|
| Cr |
0.80 |
1.10 |
|
|
| Mo |
0.45 |
0.65 |
|
|
| V |
0.25 |
0.35 |
|
|
| Ni |
- |
0.25 |
|
|
| Cu |
- |
0.35 |
|
|
| Lead |
- |
0.001(10PPM) |
|
|
Mechanical properties of grade AMS 6305F 17-22A AM S6305-2012
Yield Strength,Rp 0.2(MPa)
| Condition |
Min |
Max |
Similar |
Note |
|
1000 |
|
|
|
Tensile Strength,Rm(MPa)
| Condition |
Min |
Max |
Similar |
Note |
|
1250 |
|
|
|
Impact,Kv/Ku(J)
| Condition |
Min |
Max |
Similar |
Note |
Elongation,A(%)
| Condition |
Min |
Max |
Similar |
Note |
|
15 |
|
|
|
Reduction of area,(%)
| Condition |
Min |
Max |
Similar |
Note |
Hardness
| Condition |
Type |
Min |
Max |
Similar |
Note |
|
HB |
355 |
|
|
|
Steel, Heat-Resistant, Bars, Forgings, and Tubing 0.95Cr - 0.55Mo - 0.30V (0.40 - 0.50C) Vacuum Arc Remelted.
Melting Practice
Steel shall be multiple melted using consumable electrode vacuum practice (VAR) in the remelt cycle.
Macrostructure
Visual examination of transverse full cross-sections from bars, billets, tube rounds (solid, not hollow), and forging stock,
etched in hot hydrochloric acid in accordance with ASTM A 604, shall show no pipe or cracks. Porosity, segregation, inclusions, and other imperfections shall be no worse than the macrographs of ASTM A 604 shown in Table 2.
Average Grain Size of Bars, Forgings and Tubing
Shall be ASTM No. 5 or finer, determined in accordance with ASTM E 112.
AMS 6305F 17-22A - Form of Supply
| Product type |
Products |
Dimension |
Processes |
Deliver Status |
| Plates / Sheets |
Plates / Sheets |
0.08-200mm(T)*W*L |
Forging, hot rolling and cold rolling |
Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar |
Round Bar, Flat Bar, Square Bar |
Φ8-1200mm*L |
Forging, hot rolling and cold rolling, Cast |
Black, Rough Turning, Shot Blasting, |
| Coil / Strip |
Steel Coil /Steel Strip |
0.03-16.0x1200mm |
Cold-Rolled & Hot-Rolled |
Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes |
Seamless Pipes/Tubes, Welded Pipes/Tubes |
OD:6-219mm x WT:0.5-20.0mm |
Hot extrusion, Cold Drawn, Welded |
Annealed, Solution and Aging, Q+T, ACID-WASHED |
Cross Reference Table(Equivalent Grade)
| Grade |
Standard |
Country |
Application |
| AMS 6305F 17-22A |
AMS |
USA |
Steel, Heat-Resistant, Bars, Forgings, and Tubing 0.95Cr - 0.55Mo - 0.30V (0.40 - 0.50C) Vacuum Arc Remelted |
| AMS 6305E 17-22A |
AMS |
USA |
Steel, Heat-Resistant, Bars, Forgings, and Tubing 0.95Cr - 0.55Mo - 0.30V (0.40 - 0.50C) Vacuum Arc Remelted |