GB GH1015 Details
GB GH1015 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | GH1015 | China - GB , GB/T 14992 (2005) - Classification and designation for superalloys and high temperature intermetallic materials |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.08 | ||
| Cr | 19.0 | 22.0 | ||
| Mo | 2.50 | 3.20 | ||
| Ni | 34.0 | 39.0 | ||
| W | 4.80 | 5.80 | ||
| Nb | 1.10 | 1.60 | ||
| Si | - | 0.60 | ||
| Mn | - | 1.50 | ||
| P | - | 0.020 | ||
| S | - | 0.015 | ||
| B | - | 0.01 | ||
| Ce | - | 0.05 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 453 (≥) | 443 (≥) | 12 | 42 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 414 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 388 (≥) | 998 (≥) | 34 | 23 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 491 | 889 | 173 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH1015 | GB | China | Solid solution strengthening type iron base alloy |