GB GH1035 Details

Tags

GH1035 Application:Classification and designation for superalloys and high temperature intermetallic materials

Category Type Grade Designations
Grades Stainless Steels GH1035 China - GB , GB/T 14992 (2005) - Classification and designation for superalloys and high temperature intermetallic materials
GB/T 14995 (2010) - Hot-rolled superalloy sheets
GB/T 14996 (2010) - Cold-Rolled heat-resisting superalloy sheets

Chemical composition(wt.%) of GH1035 grade: GB/T 14992 (2005)

Elements Min.(≥) Max.(≤) Similar Remarks
C 0.06 0.12
Cr 20.0 23.0
Ni 35.0 40.0
W 2.50 3.50
Al - 0.50
Nb 1.20 1.70
Ti 0.70 1.20
Si - 0.80
Mn - 0.70
P - 0.030
S - 0.020
Ce - 0.05

Mechanical properties of grade GH1035 GB/T 14992 (2005)

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
943 (≥) 784 (≥) 21 13 41 Solution and Aging, Annealing, Ausaging, Q+T,etc 233

Physical properties of grade GH1035 GB/T 14992 (2005)

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
586 (≥) 588 (≥) 13 34 42 Solution and Aging, Annealing, Ausaging, Q+T,etc 131
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
523 226 898

GH1035 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
GH1035 GB China
Classification and designation for superalloys and high temperature intermetallic materials