GH1040 Enquiry | Print this page
GB GH1040 Details
GB GH1040 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | GH1040 | China - GB , GB/T 14992 (2005) - Classification and designation for superalloys and high temperature intermetallic materials GB/T 14994 (2008) - Cold brawn heat-resisting superalloy bars |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.12 | ||
| Cr | 15.0 | 17.5 | ||
| Mo | 5.50 | 7.00 | ||
| Ni | 24.0 | 27.0 | ||
| Si | 0.50 | 1.00 | ||
| Mn | 1.00 | 2.00 | ||
| P | - | 0.030 | ||
| S | - | 0.020 | ||
| N | 0.10 | 0.20 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 743 (≥) | 758 (≥) | 24 | 21 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 232 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 958 (≥) | 375 (≥) | 23 | 22 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 343 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 795 | 277 | 369 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| GH1040 | GB | China | Classification and designation for superalloys and high temperature intermetallic materials |