00Cr19Ni10 Enquiry | Print this page
GB 00Cr19Ni10 Details
GB 00Cr19Ni10 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | 00Cr19Ni10 | Austenite | China - GB , GB 13296 (2007) - Seamless stainless steel tubes for boiler and heat exchanger GB/T 1220 (1992) - Stainless steel bars GB/T 12770 (2002) - Welded stainless steel tubes for machine structures GB/T 12771 (2000) - Welded stainless steel pipes for liquid delivery GB/T 14975 (2002) - Stainless steel seamless tubes for structures GB/T 14976 (2002) - Stainless steel seamless tubes for fluid transport GB/T 3090 (2000) - Stainless steel small diameter seamless steel tubes GB/T 3280 (2007) - Cold rolled stainless steel sheets and plates GB/T 4237 (1992) - Hot rolled stainless steel sheets and plates GB/T 4239 (1991) - Cold rolled stainless steel and heat resisting steel strips GB/T 4356 (2002) - Stainless steel wire rods JB 4728 (2000) - Stainless Steel Forgings for Pressure Vessels |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.030 | ||
| Si | - | 1.00 | ||
| Mn | - | 2.00 | ||
| P | - | 0.035 | ||
| S | - | 0.030 | ||
| Ni | 8.00 | 12.00 | ||
| Cr | 18.00 | 20.00 |
GB 13296 (2007) Seamless stainless steel tubes for boiler and heat exchanger
Austenitic steel; Allowable stress data source: GB 150.2:2011.
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 843 (≥) | 241 (≥) | 23 | 24 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 342 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 874 (≥) | 584 (≥) | 22 | 42 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 111 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 765 | 511 | 255 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| 00Cr19Ni10 | GB | China | Carbon content lower than 0Cr19ni9 steel, excellent intergranular corrosion resistance, is used for welding after the class is not processed parts |