A 565 619 Enquiry | Print this page
SAE A 565 619 Details
SAE A 565 619 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | A 565 619 | Martensite | USA - SAE , A 565/A 565M (2010) - Martensitic Stainless Steel Bars for High-Temperature Service |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.27 | 0.32 | ||
| Si | - | 0.50 | ||
| Mn | 0.95 | 1.35 | ||
| P | - | 0.025 | ||
| S | - | 0.025 | ||
| Cr | 11.0 | 12.0 | ||
| Ni | - | 0.50 | ||
| Mo | 2.50 | 3.00 | ||
| V | 0.20 | 0.30 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 214 (≥) | 167 (≥) | 32 | 34 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 231 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 811 (≥) | 446 (≥) | 43 | 13 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 344 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 543 | 256 | 532 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| A 565 S42300 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| S42300 | AISI | USA | Martensitic Chromium Molybdenum Vanadium Stainless Steel |
| A 565 619 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| A 959 Type 619 | SAE | USA | Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels |
| A 565 S42300 | SAE | USA | Martensitic Stainless Steel Bars for High-Temperature Service |
| S42300 | AISI | USA | Martensitic Chromium Molybdenum Vanadium Stainless Steel |