B 408 N08811 Application:Nickel-Iron-Chromium Alloy Rod and Bar
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | B 408 N08811 | Precipitation-Hardening | USA - SAE , B 408 (2011) - Nickel-Iron-Chromium Alloy Rod and Bar |
Chemical composition(wt.%) of B 408 N08811 grade: B 408 (2011)
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.01 | ||
| Si | - | 0.05 | ||
| Mn | - | 1.50 | ||
| P | - | 0.04 | ||
| S | - | 0.01 | ||
| Ni | - | remaining | ||
| Cr | 0.50 | 1.50 | ||
| Al | 0.10 | 0.50 | ||
| Cu | - | 0.50 | ||
| Ti | - | - | ||
| Fe | 1.00 | 6.00 | ||
| Mo | 26.00 | 30.00 | ||
| Co | - | 2.50 |
Mechanical properties of grade B 408 N08811 B 408 (2011)
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 414 (≥) | 164 (≥) | 44 | 14 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 |
Physical properties of grade B 408 N08811 B 408 (2011)
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 283 (≥) | 935 (≥) | 32 | 13 | 34 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 221 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 762 | 682 | 643 |
B 408 N08811 - Form of Supply
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Cross Reference Table(Equivalent Grade)
| Grade | Standard | Country | Application |
|---|---|---|---|
| B 402 C70600 | SAE | USA | Copper-nickel alloy plate and sheet for pressure vessels |
| B 402 C71500 | SAE | USA | Copper-nickel alloy plate and sheet for pressure vessels |
| B 402 C72200 | SAE | USA | Copper-nickel alloy plate and sheet for pressure vessels |
| B 403 AM100A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 AZ81A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 AZ91C | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 AZ91E | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 AZ92A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 AZ92A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 EQ21A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 EZ33A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 K1A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 QE22A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 ZE41A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 403 ZK61A | SAE | USA | Magnesium-Alloy Investment Castings |
| B 407 N06811 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
| B 407 N08120 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
| B 407 N08801 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
| B 407 N08810 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
| B 407 N08811 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |