B 472 N10629 Enquiry | Print this page
SAE B 472 N10629 Details
SAE B 472 N10629 Standard Download
Category | Type | Grade | Microstructure | Designations |
---|---|---|---|---|
Grades | Stainless Steels | B 472 N10629 | Precipitation-Hardening | USA - SAE , B 472 (2010) - Standard Specification for Nickel Alloy Billets and Bars for Reforging |
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 0.01 | ||
Si | - | 0.05 | ||
Mn | - | 1.50 | ||
P | - | 0.04 | ||
S | - | 0.01 | ||
Ni | - | remaining | ||
Cr | 0.50 | 1.50 | ||
Al | 0.10 | 0.50 | ||
Cu | - | 0.50 | ||
Ti | - | - | ||
Fe | 1.00 | 6.00 | ||
Mo | 26.00 | 30.00 | ||
Co | - | 2.50 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
183 (≥) | 563 (≥) | 42 | 21 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 134 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
993 (≥) | 689 (≥) | 24 | 32 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
738 | 547 | 256 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
B 402 C70600 | SAE | USA | Copper-nickel alloy plate and sheet for pressure vessels |
B 402 C71500 | SAE | USA | Copper-nickel alloy plate and sheet for pressure vessels |
B 402 C72200 | SAE | USA | Copper-nickel alloy plate and sheet for pressure vessels |
B 403 AM100A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 AZ81A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 AZ91C | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 AZ91E | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 AZ92A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 AZ92A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 EQ21A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 EZ33A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 K1A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 QE22A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 ZE41A | SAE | USA | Magnesium-Alloy Investment Castings |
B 403 ZK61A | SAE | USA | Magnesium-Alloy Investment Castings |
B 407 N06811 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
B 407 N08120 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
B 407 N08801 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
B 407 N08810 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |
B 407 N08811 | SAE | USA | Nickel-Iron-Chromium Alloy Seamless Pipe and Tube |