SUS 410 TiTB Enquiry | Print this page
JIS SUS 410 TiTB Details
JIS SUS 410 TiTB Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | SUS 410 TiTB | Martensite | Japan - JIS , G 3463 (2012) - Stainless steel boiler and heat exchanger tubes |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.04 | ||
| S | - | 0.03 | ||
| Cr | 11.50 | 13.50 | ||
| Ni | - | 0.60 | ||
| Mo | - | - | ||
| N | - | - |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 114 (≥) | 587 (≥) | 21 | 34 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 344 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 396 (≥) | 457 (≥) | 21 | 14 | 43 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 421 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 376 | 421 | 294 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| SUS 410L | JIS | Japan | Stainless steel bars |
| SUS 410L | JIS | Japan | Hot-rolled stainless steel plates, sheet and strip |
| SUS 410L | JIS | Japan | Cold-rolled stainless steel plate, sheet and strip |
| SUS 410L | JIS | Japan | Heat-resisting steel bars and wire rods |
| SUS 410L | JIS | Japan | Heat-resisting steel plate, sheet and strip |
| SUS 410L | JIS | Japan | Stainless steel bars for concrete reinforcement |
| SUS 410 | JIS | Japan | Stainless steel bars |
| SUS 410 | JIS | Japan | Hot-rolled stainless steel plates, sheet and strip |
| SUS 410 | JIS | Japan | Cold-rolled stainless steel plate, sheet and strip |
| SUS 410 | JIS | Japan | Stainless steel wire rods |
| SUS 410 | JIS | Japan | Stainless steel wires |
| SUS 410 | JIS | Japan | Heat-resisting steel bars and wire rods |
| SUS 410 | JIS | Japan | Heat-resisting steel plate, sheet and strip |
| SUS 410 | JIS | Japan | Cold finished stainless steel bars |
| SUS 410 | JIS | Japan | Stainless steel bars for concrete reinforcement |
| SUS 410 F2 | JIS | Japan | Stainless steel bars |
| SUS 410 F2 | JIS | Japan | Stainless steel wire rods |
| SUS 410 F2 | JIS | Japan | Stainless steel wires |
| SUS 410 F2 | JIS | Japan | Cold finished stainless steel bars |
| SUS 410 FB | JIS | Japan | Stainless steel blooms and billets for forgings |