Location » Home » Grades > Stainless Steels > SUS 347HTP

JIS SUS 347HTP Details

Tags

SUS 347HTP Application:Stainless steel pipes

Category Type Grade Microstructure Designations
Grades Stainless Steels SUS 347HTP Austenite Japan - JIS , G 3459 (2012) - Stainless steel pipes

Chemical composition(wt.%) of SUS 347HTP grade: G 3459 (2012)

Elements Min.(≥) Max.(≤) Similar Remarks
C 0.04 0.10
Si - 1.00
Mn - 2.00
P - 0.03
S - 0.03
Cr 17.00 20.00
Ni 9.00 13.00
Mo - -
Nb 8×C% 1.00
Stainless steel pipes

Mechanical properties of grade SUS 347HTP G 3459 (2012)

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
737 (≥) 978 (≥) 22 43 13 Solution and Aging, Annealing, Ausaging, Q+T,etc 232

Physical properties of grade SUS 347HTP G 3459 (2012)

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
567 (≥) 338 (≥) 12 23 13 Solution and Aging, Annealing, Ausaging, Q+T,etc 244
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
747 282 367

SUS 347HTP - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED