X5CrNiCuNb16-4 Enquiry | Print this page
B.S. X5CrNiCuNb16-4 Details
B.S. X5CrNiCuNb16-4 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | X5CrNiCuNb16-4 | Precipitation-Hardening | UK - B.S. , BS EN 10088-1 - Stainless steels - Part 1: List of stainless steels BS EN 10088-2 - Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes BS EN 10088-3 - Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes BS EN 10088-4 - Stainless steels - Part 4: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for construction purposes BS EN 10088-5 - Stainless steels - Part 5: Technical delivery conditions for bars, rods, wire, sections and bright products of corrosion resisting steels for construction purposes BS EN 10250-4 - Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.07 | ||
| Si | - | 0.70 | ||
| Mn | - | 1.50 | ||
| P | - | 0.04 | ||
| S | - | 0.015 | ||
| Cr | 15.00 | 17.00 | ||
| Ni | 3.00 | 5.00 | ||
| Mo | - | 0.60 | ||
| Nb+Ta | 5×C | 0.45 | ||
| Cu | 3.00 | 5.00 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 991 (≥) | 594 (≥) | 43 | 41 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 441 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 896 (≥) | 614 (≥) | 23 | 13 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 852 | 154 | 643 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X5CrNiCuNb16-4 | B.S. | UK | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| 1.4542 | B.S. | UK | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| X5CrNiCuNb16-4 | AFNOR | France | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| 1.4542 | AFNOR | France | Open die steel forgings for general engineering purposes - Part 4: Stainless steels |
| X5CrNiCuNb16-4 | ISO | International | Stainless steels - Chemical composition |
| 17-4PH, 1.4542, X5CrNiCuNb16-4 | AMS | USA | Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) |