HR3 Enquiry | Print this page
B.S. HR3 Details
B.S. HR3 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | HR3 | UK - B.S. , BS HR 3 - Specification for nickel-cobalt-chromium-molybdenum-aluminium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 14.8, Mo 5, Al 4.7, Ti 1.2) BS 2HR 3 (2010) - Specification for nickel-cobalt-chromium-molybdenum-aluminium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 14.8, Mo 5, Al 4.8, Ti 1.2) |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.12 | 0.17 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | - | ||
| S | - | 0.015 | ||
| Cr | 14.00 | 15.70 | ||
| Ni | - | remaining | ||
| Mo | 4.50 | 5.50 | ||
| Co | 18.00 | 22.00 | ||
| Ti | 0.90 | 1.50 | ||
| Fe | - | 1.00 | ||
| Al | 4.50 | 4.90 | ||
| Cu | - | 0.20 | ||
| B | 0.0030 | 0.0100 | ||
| Bi | - | 0.0001 | ||
| Pb | - | 0.0015 | ||
| Ag | - | 0.0005 | ||
| Zr | - | 0.15 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 544 (≥) | 754 (≥) | 31 | 31 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 321 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 645 (≥) | 931 (≥) | 11 | 44 | 44 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 423 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 139 | 212 | 575 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| HR3 | B.S. | UK | Specification for nickel-cobalt-chromium-molybdenum-aluminium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Co 20, Cr 14.8, Mo 5, Al 4.8, Ti 1.2) |