HR5 Enquiry | Print this page
B.S. HR5 Details
B.S. HR5 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | HR5 | UK - B.S. , BS 2HR 5 (2010) - Specification for nickel-chromium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Cr 19.5, Ti 0.4) BS HR 5 - Specification for nickel-chromium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Cr 19.5, Ti 0.4) |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.08 | 0.15 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | - | ||
| S | - | 0.020 | ||
| Cr | 18.00 | 21.00 | ||
| Ni | - | remaining | ||
| Mo | - | - | ||
| Co | - | 5.00 | ||
| Ti | 0.20 | 0.60 | ||
| Fe | - | 5.00 | ||
| Al | - | - | ||
| Cu | - | 0.50 | ||
| B | - | - | ||
| Bi | - | - | ||
| Pb | - | 0.0050 | ||
| Ag | - | - |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 849 (≥) | 181 (≥) | 13 | 22 | 22 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 114 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 638 (≥) | 115 (≥) | 43 | 43 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 993 | 964 | 853 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| HR5 | B.S. | UK | Specification for nickel-chromium-titanium heat-resisting alloy billets, bars, forgings and parts (nickel base, Cr 19.5, Ti 0.4) |
| HR50F45 | B.S. | UK | Steel plate, sheet and strip. Carbon and carbon-manganese plate, sheet and strip. Specification for hot rolled wide material based on specified minimum strength |
| HR50/35 | B.S. | UK | Steel plate, sheet and strip. Carbon and carbon-manganese plate, sheet and strip. Specification for hot rolled wide material based on specified minimum strength |
| HR50/45 | B.S. | UK | Steel plate, sheet and strip. Carbon and carbon-manganese plate, sheet and strip. Specification for hot rolled wide material based on specified minimum strength |
| HR51 | B.S. | UK | Specification for heat-resisting alloy billets, bars, forgings and parts (Ni 25.5, Cr 14.7, Ti 2, Mn 1.5, Mo 1.2, Si 0.7, V 0.3, Fe remainder) |
| HR52 | B.S. | UK | Specification for heat-resisting alloy billets, bars, forgings and parts (Ni 25.5, Cr 14.7, Ti 1.8, Mn 1.5, Mo 1.2, V 0.3, Fe remainder) |
| HR53 | B.S. | UK | Specification for nickel-iron-chromium-molybdenum-titanium heat-resisting alloy billets, bars, forgings and parts (Ni/Co 42.5, Cr 12.5, Mo 5.8, Ti 3.0, Fe remainder) |
| HR55 | B.S. | UK | Specification for nickel-iron-chromium-molybdenum-aluminium-titanium heat-resisting alloy billets, bars, forgings and parts (Ni/Co 43.5, Cr 16.5, Mo 3.3, Al 1.2, Ti 1.2, Fe remainder) |
| 2HR501 | B.S. | UK | Specification for nickel-chromium-cobalt-titanium- aluminium heat-resisting alloy cold drawn wire for springs and springs (Nickel base, Cr 19.5, Co 18.0, Ti 2.5, Al 1.5) |