Location » Home » Grades > Stainless Steels > HR404

HR404 Enquiry | Print this page

B.S. HR404 Details

B.S. HR404 Standard Download

Tags

HR404 Application:Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Category Type Grade Designations
Grades Stainless Steels HR404 UK - B.S. , BS HR 404 (1973) - Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)
BS 2HR 404 (2011) - Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Chemical composition(wt.%) of HR404 grade: BS HR 404 (1973)

Elements Min.（≥） Max.（≤） Similar Remarks
C 0.04 0.08
Si - 0.40
Mn - 0.60
P - -
S - 0.007
Cr 19.00 21.00
Ni - remaining
Mo 5.60 6.10
Co 19.00 21.00
Ti 1.90 2.40
Fe - 0.70
Al 0.30 0.60
Ag - 0.0005
Al+Ti 2.40 2.80
Cu - 0.20
B - 0.0050
Bi - 0.0001
Pb - 0.002
Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Mechanical properties of grade HR404 BS HR 404 (1973)

Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
455 (≥) 593 (≥) 44 13 23 Solution and Aging, Annealing, Ausaging, Q+T,etc 414

Physical properties of grade HR404 BS HR 404 (1973)

Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
855 (≥) 191 (≥) 14 22 41 Solution and Aging, Annealing, Ausaging, Q+T,etc 141
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
896 897 434

HR404 - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
HR404 B.S. UK
Specification for nickel-cobalt-chromium-molybdenum-titanium-aluminium heat-resisting alloy cold worked solution treated seamless tubes (nickel base, Co 20, Cr 20, Mo 5.9, Ti 2.1, Al 0.5)

Enquiry