Z3CTNb18 Enquiry | Print this page
AFNOR Z3CTNb18 Details
AFNOR Z3CTNb18 Standard Download
Category | Type | Grade | Designations |
---|---|---|---|
Grades | Stainless Steels | Z3CTNb18 | France - AFNOR , NF A 35-573 - Stainless steels for general purposes. Plates, wide strips and strips NF A 35-578 - Iron and steel. Stainless steel for high temperature application |
Elements | Min.(≥) | Max.(≤) | Similar | Remarks |
---|---|---|---|---|
C | - | 0.030 | ||
Si | - | 0.75 | ||
Mn | - | 0.08 | ||
P | - | 0.030 | ||
S | - | 0.015 | ||
Cr | 17.50 | 18.50 | ||
Mo | - | - | ||
Ni | - | - | ||
N | - | 0.025 | ||
Ti | 0.10 | 0.50 | ||
Nb | 9×C | 0.30 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
612 (≥) | 878 (≥) | 42 | 31 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
518 (≥) | 956 (≥) | 13 | 44 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 122 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
922 | 642 | 116 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
Grade | Standard | Country | Application |
---|---|---|---|
Z3CTNb18 | AFNOR | France | Iron and steel. Stainless steel for high temperature application |