Z20C13CI Enquiry | Print this page
AFNOR Z20C13CI Details
AFNOR Z20C13CI Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | Z20C13CI | France - AFNOR , NF A 35-595 - Iron and steel. Cutlery stainless steel |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.18 | 0.23 | ||
| Si | - | 0.75 | ||
| Mn | - | 1.00 | ||
| P | - | 0.040 | ||
| S | - | 0.015 | ||
| Cr | 12.00 | 14.00 | ||
| Mo | - | - | ||
| Ni | - | - |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 684 (≥) | 465 (≥) | 11 | 23 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 212 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 866 (≥) | 883 (≥) | 33 | 14 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 121 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 495 | 923 | 137 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| Z20C13 | AFNOR | France | Surgical instruments. Haemostatic forceps. Stainless steel. Chemical composition and hardness |
| Z20C13CI | AFNOR | France | Iron and steel. Cutlery stainless steel |
| Z20C13F | AFNOR | France | General purpose forgings. Stainless steels |
| Z20C13M | AFNOR | France | Steel castings |