Location » Home » Grades > Stainless Steels > X3Cr17E

ISO X3Cr17E Details

Tags

X3Cr17E Application:Steels for cold heading and cold extruding

Category Type Grade Microstructure Designations
Grades Stainless Steels X3Cr17E Ferrite International - ISO , ISO 4954 - Steels for cold heading and cold extruding

Chemical composition(wt.%) of X3Cr17E grade: ISO 4954

Elements Min.(≥) Max.(≤) Similar Remarks
C - 0.04
Si - 1.00
Mn - 1.00
P - 0.040
S - 0.030
Cr 16.00 18.00
Ni - 1.00
Mo - -
Steels for cold heading and cold extruding

Mechanical properties of grade X3Cr17E ISO 4954

Proof strength
Rp0.2 (MPa)
Tensile strength
Rm (MPa)
Impact energy
KV (J)
Elongation at fracture
A (%)
Reduction in cross section on fracture
Z (%)
As-Heat-Treated Condition Brinell hardness (HBW)
291 (≥) 351 (≥) 23 34 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 443

Physical properties of grade X3Cr17E ISO 4954

Property Density
kg/dm3
Temperature T
°C/F
Specific heat
J / kgK
Thermal conductivity
W/mK
Electric resistance
µΩ·cm
Modulus of elasticity
kN/mm2
Expansion rate
349 (≥) 386 (≥) 14 24 12 Solution and Aging, Annealing, Ausaging, Q+T,etc 424
Temp.
°C/°F
Creep strain limit
(10000h)
(Rp1,0) N/mm2
Creep rupture strength
(10000h)
(Rp1,0) N/mm2
538 777 563

X3Cr17E - Form of Supply

Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Cross Reference Table(Equivalent Grade)

Grade Standard Country Application
X3Cr17E ISO International
Steels for cold heading and cold extruding