X12CrNiMoV12-3 Enquiry | Print this page
ISO X12CrNiMoV12-3 Details
ISO X12CrNiMoV12-3 Standard Download
| Category | Type | Grade | Microstructure | Designations |
|---|---|---|---|---|
| Grades | Stainless Steels | X12CrNiMoV12-3 | Bainite | International - ISO , ISO/TR 4956 - Wrought steels for use at elevated temperatures in engines |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | 0.08 | 0.15 | ||
| Si | - | 0.35 | ||
| Mn | 0.50 | 0.90 | ||
| P | - | 0.030 | ||
| S | - | 0.025 | ||
| Cr | 11.00 | 12.50 | ||
| Mo | 1.50 | 2.00 | ||
| Ni | 2.00 | 3.00 | ||
| V | 0.25 | 0.40 | ||
| N | 0.02 | 0.04 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 675 (≥) | 172 (≥) | 34 | 32 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 951 (≥) | 483 (≥) | 23 | 12 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 144 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 763 | 474 | 834 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X20CrMoNiNbV11-1 | ISO | International | Wrought steels for use at elevated temperatures in engines |
| X12CrNiMoV12-3 | ISO | International | Wrought steels for use at elevated temperatures in engines |