AISI504 Enquiry | Print this page
AISI AISI504 Details
AISI AISI504 Standard Download
| Category | Type | Grade | Designations |
|---|---|---|---|
| Grades | Stainless Steels | AISI504 | USA - AISI , |
| Elements | Min.（≥） | Max.（≤） | Similar | Remarks |
|---|---|---|---|---|
| C | - | 0.15 | ||
| Si | - | 1.00 | ||
| Mn | - | 1.00 | ||
| P | - | 0.04 | ||
| S | - | 0.04 | ||
| Cr | 8.00 | 10.00 | ||
| Mo | 0.90 | 1.10 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 317 (≥) | 525 (≥) | 12 | 33 | 31 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 313 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 585 (≥) | 991 (≥) | 32 | 13 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 423 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 159 | 516 | 972 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| S50400 | AISI | USA | Stainless Steel |
| AISI504 | AISI | USA | AISI504 |
| S50400 | UNS | USA | Alloy steels are designated by AISI four-digit numbers and are more susceptible to heat and mechanical treatments than carbon steels. They comprise different kinds of steels having compositions which exceed the limitations of Va, Cr, Si, Ni, Mo, C and B i |